ppr female tee pipe fittings

***Features

Material: PPR HYOSUNG R200P from Korea,58-3A cooper for brass insert

Sizes: 20x1/2" - 63x2"

Pressure Rating:2.5MPa

Standard: ISO 15874: 2003, DIN8077-8078

Production temperature: -40 - +95°C

Certification: ISO9001, ISO14001, AENOR

Color:Green,White,Grey etc

Size:20mmx1/2"-63mmx2"

***Applications:

cold or hot water supply, heating system including flooring heating, wall heating and radiant,

central air conditioning and industrial liquids transportation. 

***Advantages:

High temperature resistance: the maximum sustained working temperature is up to 70°C, the

maximum transient temperature is up to 95°C

Heat preservation: low thermal conductivity result in preserving heat

Non-toxic: no heavy metal additives, would not be covered with dirt or contaminated by bacterium

Lower installation costs: light weight and ease of installation can reduce installation costs

Higher flow capacity: smooth interior walls result in low pressure loss and high volume

***Size:

Size(mm)	pcs/carton	MOQ(cartons)	Remarks
20x1/2"	300	4
20x3/4"	240	4
25x1/2"	300	4
25x3/4"	240	4
32x1/2"	200	5
32x3/4"	180	6
32x1'	120	6
40x11/4"	70	5
50x11/2"	72	5
63x2"	36	5

Connection method PP-R pipes and fittings for the general use of hot melt or fused connection, connect

the pipes and fittings while heating the critical melt into, and then the pipe immediately straight

insert fittings in good pipeline contact performance welding complete, the success rate high. But when

the weld should be careful not to shake around, time not too long. Pipe and fittings specifications to

unity. In addition, the welding equipment must be thermostatically controlled, high temperature welding

impermeable, easy to leak, the temperature is too low, the welding speed is slow, laborious and time

consuming.

The steps of welding:

1.Use special pipe cutter to cut the pipe, the cut should be smooth and free of burrs.

2.Clean the welding area of pipes and fittings, to avoid sand, dust and other damage to the joint quality.

3.And being welded pipe size with matching head assembly fuser heating, heated to 260 ℃.

4.Marked with a marker on the pipe welding depth.

5.While the pipe and pipe fittings into the welding device, the time required for heating.

6.After heating, the vertical pipe and fittings to promote and maintain more than 5 seconds,

not excessive force to prevent bending.